Fatigue behaviour study on repaired aramid fiber/epoxy composites

Ano: 2009 | Volume: 1 | Número: 2

Autores: Edson Cocchieri Botelho, Rogério Lago Mazur, Michelle Leali Costa, Geraldo Maurício Cândido, Mirabel Cerqueira Rezende

Palavras-chave: fatigue behavior, aramid/epoxy composite, structural composites, mechanical behavior

Resumo Inglês:

Aramid fiber reinforced polymer composites have been used in a wide variety of applications, such as aerospace, marine, sporting equipment and in the defense sector, due to their outstanding properties at low density. The most widely adopted procedure to investigate the repair of composites has been by repairing damages simulated in composite specimens. This work presents the structural repair influence on tensile and fatigue properties of a typical aramid fiber/epoxy composite used in the aerospace industry. According to this work, the aramid/epoxy composites with and without repair present tensile strength values of 618 and 680MPa, respectively, and tensile modulus of 26.5 and 30.1 GPa, respectively. Therefore, the fatigue results show that in loads higher than 170 MPa, both composites present a low life cycle (lower than 200,000 cycles) and the repaired aramid/epoxy composite presented low fatigue resistance in low and high cycle when compared with non-repaired composite. With these results, it is possible to observe a decrease of the measured mechanical properties of the repaired composites.